ʻO Corundum mullite refractory castable kahi ʻano o ka ikaika kiʻekiʻe unshaped refractory mea no ke kūʻai aku ma RS Company, hiki ke hoʻohana ʻia i ka kiln sima. Hiki i nā corundum mullite castables ke hana i nā waiwai kiʻekiʻe e like me ka ikaika ʻoki kiʻekiʻe, ke kūpaʻa wela kiʻekiʻe, ke kū ʻana o ka haʻalulu wela, ka ʻaʻahu a me ke kūpaʻa erosion kemika i ka uhi ʻana o ka paila mana nui a me nā mea wela kiʻekiʻe. refractory corundum mullite castable hiki ke hoʻohana 'ia i loko o ke kila umu ahi, sima kiln, aniani kapuahi, hao hana kapuahi, ceramic tunnel kiln a pela aku.
ʻO ka mea nui o ka corundum mullite castable he māmā alumini oxide aggregate, kiʻekiʻe kiʻekiʻe maʻemaʻe maoli mullite ore, a me ka calcium aluminate cement e like me ka mea hoʻopaʻa. Hana ʻia ka corundum mullite refractory castable ma o ke ahi wela kiʻekiʻe e ka umu ʻoihana holomua. ʻO ka ikaika flexural corundum mullite a me ka ikaika compressive e hoʻonui mua a emi iho a laila me ka piʻi ʻana o ka mahana mālama wela. A inā he 5% ka mana o ka alumina micro, hiki i ka ikaika flexural i luna.
ʻOi aku ka ʻike o Al2O3 ma mua o 90%, a ʻo ka corundum mullite insulation castable me ka corundum e like me ka pae aniani nui i hui pū ʻia me nā dispersants kūpono, nā coagulants, nā fibers stainless steel, i hoʻohui ʻia e like me ke ʻano koʻikoʻi. ʻO Refractory corundum mullite castable he nui nā hiʻohiʻona, e like me ka ikaika wela kiʻekiʻe, ka pale ʻana a me ka anti-scour, ka hoʻokele wela kiʻekiʻe, ke kūpaʻa haʻalulu wela, ke kūpaʻa corrosion, ke sila maikaʻi a me ka condensation mua.
'ikamu | NM-1 | NM-2 | NM-3 |
Al2O3 % ≥ | 75 | 80 | 85 |
CaO % ≤ | 2 | 2 | 2 |
ʻAno nui g/cm3 > | 2.75 | 2.8 | 2.9 |
ʻO ka ikaika ʻohi Mpa (1400 ℃, 3h) | >95 | >105 | >110 |
Modulus o ka rupture Mpa(1400 ℃, 3h) | >13.5 | >15.0 | >16.0 |
ʻO ka poho abrasion wela o ka lumi cm3 | <8.5 | <7.3 | <6 |
0.2MPa, refractoriness ma lalo o ka ukana hoʻomaka wela ℃ | >1490 | >1530 | >1560 |
ʻO ke kūpaʻa haʻalulu wela (900 ℃, hoʻolili wai)/manawa | >20 | >20 | >20 |
Max. mahana hana ℃ | 1550 | 1600 | 1600 |
Hoʻomaʻamaʻa hou i ka helu hoʻololi laina % | <-0.3 | <-0.2 | <-0.2 |
<-0.2